Chrome Corundum Casting Castables

Chrome corundum casting castables (also called chromium corundum refractory castables or chromium corundum castables), which is with chrome oxide and corundum as the main raw materials, through high pressure forming, high-temperature firing and made of alumina and chrome oxide content is not less than 90%, chromium oxide content is not more than 50% of the shaped refractory products.

Send Email Inquiry Now

Introduction of Chrome Corundum Casting Castables

The main compositions of chrome corundum casting castables are Al2O3 and Cr2O3, these two components can form a continuous solid solution. adding Cr2O3 to the Al2O3 single-phase material not only increases the thermal ability of the material in a high-temperature atmosphere but also increases refractoriness for the chromium and corundum combined castables. the melting point of this solid solution is at a high temperature above 2050 °C, which has high-temperature resistance, washing, and abrasion resistance. Cr2O3 can improve the slag corrosion resistance and spalling performance of refractory products. Therefore, the service life of chrome corundum casting castables is longer than normal corundum castables.

Properties of Chrome Corundum Casting Castables

High abrasion-resistant ability, corrosion resistance,

High refractoriness under load(1700℃) and so on.

High compressive strength and high stability of the high-temperature lining.

Large bulk density, overall lining resistance to slag erosion, and strong permeability.

Anti-solid particles, dust, high-temperature gas flushing.

Small mechanical abrasion resistance.

Not affected by reducing gases such as H2 and CO.

The construction is convenient. It can be cast into an integral lining, or it can be poured into prefabricated blocks or prefabricated parts.

Characteristics of Chrome Corundum Casting Castables

1. High-temperature resistance and high operating temperature.

2. Under 0.2mpa pressure, the softening temperature of the load is high.

3. High-temperature volume stability, high strength.

4. Anti-slag slag has strong chemical corrosion.

5. The construction is convenient. It can be cast into a seamless inner lining, or it can be prefabricated into cast precast blocks.

6. The overall structure is stable and resistant to spalling.

7. Quenching and rapid heat resistance, excellent thermal shock resistance.

8. High-strength explosion-proof, to prevent the cracking or peeling of the surface of the cast lining due to baking.

Production Process of Chrome Corundum Casting Castables

Chrome corundum casting castables are made of α-Al2O3 as raw material, adding the appropriate amount of chromium oxide powder and chrome corundum clinker fine powder, forming and firing at high temperatures. It can also be prepared by mud casting. α-Al2O3 powder and chromium oxide powder are mixed evenly. Thickeners are made by adding glue and organic binders. At the same time, part of the chrome corundum clinker is added, and the castables are made by the grouting method.

Applications of Chrome Corundum Casting Castables

It is widely used in kilns, furnaces, and thermal equipment of metallurgy, petroleum industry, chemical industry, building material, machinery, etc.

Cr2O3 in chrome corundum casting castables has very low solubility in molten slag, as Cr2O3 can enhance the viscosity of molten slag, then the dissolution erosion rate of chrome corundum castable is reduced. So chrome corundum castable is important refractory material used for oxidizing atmosphere-melting furnace working lining.

Packing of Chrome Corundum Casting Castables

Plastic bag(25kg), Kraft bag (25 kg), Plastic Ton bag(1 ton);

1 ton on the pallet with plastic film & bundle belts.

Per your requests

Physical Parameters

Item		XHJCCC60	XHJCCC75	XHJCCC80	XHJCCC85	XHJCCC90
Cr₂O₃（%）		≥8	≥15	≥10	≥8	≥5
AL₂O₃（%）		≥60	≥75	≥80	≥85	≥90
Fe₂O₃ (%)		≤0.5	≤0.5	≤0.4	≤0.4	≤0.3
Apparent porosity（%）		≤18	≤18	≤18	≤18	≤18
Bulk density	(g/cm³)	≥2.8	≥3.2	≥3.0	≥2.9	≥3.1
Modulus of Rupture	(MPa) 110℃*24H	8	9	10	10	11
Modulus of Rupture	(MPa) 1500℃*3H	12	13	15	15	16
Cold crushing strength	(MPa) 110℃*24H	≥90	≥120	≥80	≥80	≥100
Cold crushing strength	(MPa) 1500℃*3H	≥150	≥155	≥155	≥160	≥165
Refractoriness under load	(℃) 0.2MPa,0.6%	≥1850	≥1900	≥1950	≥1970	≥1900
Working Temperature	(℃) 0.2MPa,0.6%	≥1700	≥1730	≥1750	≥1770	≥1790
Particle size	mm.	1~0, 3.0~1.0, 5.0~3.0, 200mesh, or customized.